Guangzhou Tabard Fire-Proof Materials Co. Ltd. / Guangzhou Tabard Special Coating Engineering Co. Ltd. 

Details

Home  > PRODUCTS  > Anti-corrosion coatings > Primer > Details
CF-2 Alkyd Red Lead Anti-Rust Paint
  • CF-2 Alkyd Red Lead Anti-Rust Paint
  • Specifications
    • Product Name：CF-2 Alkyd Red Lead Anti-Rust Paint
    • Product Number：CF-2
    • 分享到：
  • Details

  • Product Description

    It is composed by alkyd resin, red lead powder, extender pigment, desiccant and solvent, with good anti-rust property, rapid drying and hard paint film.


    Design Purpose 

    Priming and rust resistance on the surface of black metal in the slight and medium corrosive industrial environment, being inapplicable for underwater position.


    Physical Parameters

    Color

    Nacarat

     

    Luster

    Lightless

     

    Theoretical spreading rate

    180g/m2, 11.10m2/L (calculated in 40μm dry film, excluding the loss)

     

    Specific gravity:

    About 2.0

     

    Drying time

    23±2℃: surface dryness≦4h, solid dryness≦24h

     

    Flash point

    38℃

     

    Storage period

    12 months

    Construction Instruction

    Mixing ratio

    Canned by single pot


    Maturing time

    Use immediately after opening and stirring uniformly


    Service life

    Unlimit


    Construction method

    Manual painting;  roller coating  


    Diluent

    X-6 Alkyd coating diluent


    Maximal dilution amount

    5%


    Tool washing

    X-6 Alkyd coating diluent


    Film coating thickness

    Wet film: 95μm                     Dry film: 60μm


    Coating interval

    Temperature of substrate

    5℃

    20℃

    30℃

    Shortest

    48h

    24h

    12h

    Longest

    Unlimit

     


    Surface treatment

    ＊If it is coated directly on the steel, the steel is required to be subjected to shot blasting or sandblasting treatment  so as to reach Grade Sa2 of Sweden Derusting Standard, or the manual derusting reaches  Grade St3;

    ＊The primer surface in the workWorkshop is required to be subjected to secondary derusting so as to reach Grade St3 of Sweden Derusting Standard.


    Construction condition

    The temperature of substrate must be 3℃ higher than dewing point, and the relative humidity must be less than 85%.

     

    Finishing paint

    Alkyd enamel paint,alkyd tempered paint;alkyd rusty red anti-rust paint, Alkyd micaceous iron anti-rust paint.

    Packing Specification

    25Kg/20L per barrel

    Considerations

    ＊This coating contains the heavy pigment particle, while constructing , this coating can be utilized after uniformly stirring thoroughly;

    ＊There is red lead inside paint film, it is inadvisable to be used in the sealed cabin where the fire work calibration must be conducted so as to prevent lead poisoning;

    ＊The red lead paint film is inadvisable to expose in the air for long term, otherwise, the paint film easily whitens or discolors.

    Safety guide  

    Avoid breathing solvent steam or paint fog for a long term; the skin and eye can’t contact this product; while constructing in the narrow place or poorly ventilated place, the forced ventilation must be provided; while constructing, the protective articles should be worn.

    Annotation

    ＊Above-said thickness of dry film and wet film refers to the index while implementing the high-pressure siphon spray;

    ＊Relevant data in this instruction is obtained from laboratory, the actual product may be slightly different from it;

    ＊If above data is changed, the data is based on the latest instruction, without prior notification.