Theoretical spreading rate

162g/m2, 8m2/L (calculated in 40μm dry film, excluding the loss)

Specific gravity:

About 1.30

Drying time

23±2℃: surface dryness:2h, solid dryness : 24h

Flash point

26℃

Storage period

12 months

Construction Instruction

Mixing ratio

Canned by single pot

Maturing time

Use immediately after opening

Service life

Unlimit

Construction method

Manual painting;  roller coating, high-pressure air-free spraying

Diluent

X-16 highly chlorined polyethylene coating diluent

Maximal dilution amount

＜5%

Spraying hole

20P20

Spraying pressure

195kg/cm2 (the spraying data is only used for reference; the adjustment may be conducted while using).

Tool washing

X-16 highly chlorined polyethylene coating diluent

Film coating thickness

Wet film: 125μm                     Dry film: 40μm

Coating interval

Surface treatment

＊The steel surface reaches Grade Sa2.5 of Sweden Derusting Standard subject to shotblasting, or reaches Grade St3 subject to manual or power tool, the surface after derusting should be coated with highly chlorined polyethylene rusty red primer within 24 hours so as to avoid producing the secondary rusting.

＊After the concrete cement mortar surface is placed and cured for a period of time so that the moisture evaporates sufficiently and the alkali salinity separates out and is eliminated thoroughly, the construction can be conducted, if there are crack, pockmark, air pore, unshelling or unevenness place, the putty may be employed for repairing evenly.

Construction condition

Prior to construction, the coating must be stirred sufficiently and uniformly.

The temperature of substrate must be 3℃ higher than dewing point.

The construction temperature of ordinary highly chlorined polyethylene anti-corrosive coating is between 0-35℃ preferentially. During construction, take notice the weather and temperature change; during rainy, foggy and snowy day, or the relative humidity is greater than 85% or the weather is scorching under direct irradiation by strong sunshine in summer, the construction can’t be conducted uniformly.

Former primer

Epoxy zinc rich workWorkshop primer, epoxy zinc powder workWorkshop primer, epoxy rusty red workWorkshop primer, inorganic zinc silicate workWorkshop primer, inorganic zinc silicate workWorkshop primer.

Finishing paint

Highly chlorined polyethylene mica iron anti-rust paint, highly chlorined polyethylene enamel paint (outdoor type), highly chlorined polyethylene enamel paint (indoor type).

Packing Specification

25Kg/20L per barrel

Remarks

The thickness of paint film may be modified according to use purpose or use area, however, the spreading rate, drying time and recoating interval may be changed correspondingly.

Considerations

＊Prior to construction, the highly chlorined polyethylene anti-corrosive coating must be stirred sufficiently and uniformly, after that, the construction can be performed.

＊The highly chlorined polyethylene heavy anti-corrosive coating may be adopted with brushing painting and roller painting construction method( spray painting may be adopted for primer), the coating shall be conducted according to crisscross sequence and remains certain speed so as to form compact and uniform coating in thickness and reduce the generation of air pore. When the brush painting is adopted, the coating frequency is inadvisable to be too much, being of three times generally. If the repeating frequency for finish paint coating is too much, the coating at the bottom or in the middle layer is easily roughed so that the coating discolors.

＊For dilution of highly chlorined polyethylene heavy anti-corrosive coating, the special-purpose diluent for highly chlorined polyethylene heavy anti-corrosive coating should be employed. While coating during construction under low temperature and after sandblasting treatment, the coating isn’t required to be diluted. When the steel surface is constructed under higher temperature condition in summer, the primer must be coated after being diluted, however, the dilution dosage must be controlled between 5%~10% of coating volume.

＊Interval time of coating for highly chlorined polyethylene heavy anti-corrosive coating; after the steel surface is subjected to first pass of primer on the anti-rusting paint, the later pass of primer, medium paint and finish paint should be coated with the specified coating interval time.

Safety guide  

The Safety guide items on the packaging label should be noticed. In addition, thesafety laws and regulations specified by relevant state or local government should also be observed. Avoid breathing solvent steam or paint fog for a long term; the skin and eye can’t contact this product; while constructing in the narrow place or poorly ventilated place, the forced ventilation must be provided; while constructing, the protective articles should be worn.

Annotation

＊Above-said thickness of dry film and wet film refers to the index while implementing the high-pressure siphon spray;

＊Relevant data in this instruction is obtained from laboratory, the actual product may be slightly different from it;

＊If above data is changed, the data is based on the latest instruction, without prior notification.